NM500 is a high-strength wear-resistant steel, which has a high wear resistance, Brinell hardness value reaches 500 (HBW) mainly in the need to wear the occasion or location to provide protection to the equipment longer life, reduced maintenance brought maintenance and downtime, and the corresponding reduction of capital investments.
GB/T24186 NM500 abrasion resistant steel plate chemical composition | Brand | C | Si | Mn | P | S | Cr | Mo | Ni | B | CEV |
| NM360 | ≤0.17 | ≤0.50 | ≤1.5 | ≤0.025 | ≤0.015 | ≤0.70 | ≤0.40 | ≤0.50 | ≤0.005 | |
| NM400 | ≤0.24 | ≤0.50 | ≤1.6 | ≤0.025 | ≤0.015 | 0.4~0.8 | 0.2~0.5 | 0.2~0.5 | ≤0.005 | |
| NM450 | ≤0.26 | ≤0.70 | ≤1.60 | ≤0.025 | ≤0.015 | ≤1.50 | ≤0.05 | ≤1.0 | ≤0.004 | |
| NM500 | ≤0.38 | ≤0.70 | ≤1.70 | ≤0.020 | ≤0.010 | ≤1.20 | ≤0.65 | ≤1.0 | Bt: 0.005-0.06 | 0.65 |
GB/T24186 NM500 abrasion resistant steel plate mechanical properties | Brand | Thickness mm | Tensile Test MPa | Hardness |
| | | YS Rel MPa | TS Rm MPa | Elongation % | |
| NM360 | 10-50 | ≥620 | 725-900 | ≥16 | 320-400 |
| NM400 | 10-50 | ≥620 | 725-900 | ≥16 | 380-460 |
| NM450 | 10-50 | 1250-1370 | 1330-1600 | ≥20 | 410-490 |
| NM500 | 10-50 | --- | ---- | ≥24 | 480-525 |
Processing Technique - Electric Furnace Steelmaking
- LF Refining
- VD Vacuum Treatment
- Continuous casting and rolling
- Accelerated Cooling
- Thermal Treatment
- Ware-house-in Inspection
Capacity: 3,000 ton per month.
Test: Chemical analysis, Metallographic, Mechnical analysis, Ultrasonic testing, Impact testing, Hardness testing, Surface quality and Dimension report.
Package: Bundle or piece.
Mill’s Test Certificate
EN 10204/3.1 with all relevant data reg. chem. composition, mech. properties and results of testing.
Heat treatment: quenching and tempering (quenching and tempering).
NM500 wear-resistant steel is widely used construction machinery, mining machinery, mining machinery, environmental protection machinery, metallurgical machinery, abrasives, bearings and other product components.